Accessory Compatibility
| Recommended | Not Recommended |
Build Plate | Cool Plate, High Temperature Plate or Textured PEI Plate | Engineering Plate |
Hotend | Hotend with Hardened Steel Nozzle (0.4 mm) Hotend with Stainless Steel Nozzle (0.2 mm, 0.4 mm) | Hotend with Hardened Steel Nozzle (0.6 mm, 0.8 mm) |
Glue | Liquid Glue / Glue Stick | / |
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
Recommended Printing Settings |
Drying Settings (Blast Drying Oven) | 55 °C,8 h |
Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
Nozzle Temperature | 210 - 240 °C |
Bed Temperature (with Glue) | 35 - 45 °C |
Printing Speed | < 250 mm/s |
Physical Properties |
Density | 1.32 g/cm³ |
Vicat Softening Temperature | 56 °C |
Heat Deflection Temperature | 53 °C |
Melting Temperature | 152 °C |
Melt Index | 20.5 ± 1.2 g/10 min |
Mechanical Properties |
Tensile Strength | 27 ± 4 MPa |
Breaking Elongation Rate | 3.5 ± 0.6 % |
Bending Modulus | 2370 ± 150 MPa |
Bending Strength | 66 ± 4 MPa |
Impact Strength | 24.5 ± 1.7 kJ/m² |
Downloads
Filament TDS
Filament MSDS
Filament RoHS
Printing Tips
• Drying conditions: 55℃ for 8 hrs. Store in a dry environment after use. Dry before use if the material absorbs moisture. For more details please refer to: Filament drying instructions on WIKI.
• PLA Silk Dual Color is a new color options of PLA Silk series, please use the default PLA Silk setting for printing. To obtain higher printing quality and higher gloss finish, please set lower printing speed.
• When printing with PLA Silk Dual Color filament, there is a small chance of filament rotation, potentially causing uneven color transitions. The A-series printers have a higher risk due to their special structure, so use of this filament with A-series printers is not recommended.