3D print strong, precise concept models and prototypes that bring your ideas to life with Formlabs’ library of Standard Resins. With a matte surface finish, opaque appearance, and precise details, prints are ready to use right off the printer. Their neutral undertone makes a great base for parts that will eventually be painted or undergo other finishing processes. Grey Resin is perfect for general-purpose prototyping and design, excellent for capturing small details. Supports print resolutions: 160, 100, 50, and 25 microns.
What's Included
Compatibility
Printer compatibility: Form 2, Form 3, Form 3B, Form 3L, Form 3BL, Form 3+, Form 3B+
Compatible with these resin tanks: Form 2 Resin Tank (PDMS), Form 2 LT Tank, Form 3/3B Resin Tank V1, Form 3/3B Resin Tank V2, Form 3/3B Resin Tank V2.1, Form 3L/3BL Resin Tank V1
Compatible with these build platforms: Form 3 Build Platform 2
Why Choose Formlabs Grey Resin
Leverage Grey Resin to iterate on high-resolution prototypes and models that capture astonishing detail without sacrificing strength.
Matte Appearance
Produce prints with smooth, opaque surfaces ideal for model making and looks-like prototyping, rivalling injection-moulded plastics.
High Part Quality
Create elegant, enticing parts without sanding, polishing, or priming.
Ease of Use
Start using your parts quickly, as Formlabs’ Standard Resins only need minimal post-processing.
Neutral Undertone
Paint or use other finishing processes to elevate your model or prototype.
Applications
Grey Resin supports high detail with a smooth, matte surface finish with great mechanical properties.
Consider Grey Resin for:
- General-purpose prototyping and design
- Models with very small features and intricate details
- Base for painted parts
- Presentation-ready pieces
Material Properties*
Ultimate Tensile Strength: 65 MPa
Tensile Modulus: 2.6 GPa
Elongation: 6%
Flexural Modulus: 2.2 GPa
Notched Izod: 25 J/m
Heat Deflection Temp @ 0.45 MPa: 73 ºC
*Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2, 100 μm, Clear settings and post-cured with 1.25 mW/cm³ of 405 nm LED light for 60 minutes at 60 °C.